Experimental characterization of laser cladding of Stellite 21 on H13 tool steel

Experimental characterization of laser cladding of Stellite 21 on H13 tool steel

 

The repair of dies and molds by using additive manufacturing techniques such as laser cladding (LC) is an important and emerging trend in tooling industry today. LC provides an alternative to the traditional deposition techniques. In order to enhance the die life, it has been observed that cladding based repair is superior to welding or thermal spraying repair techniques. In this paper, experimental study of laser cladding of H13 has been carried out. Stellite 21 steel powder has been deposited on H13 tool steel plate for repairing the die surface damage using a diode laser in conjunction with powder injection system. The microstructure of laser cladded samples has been characterized using optical microscope (OM) and scanning electron microscope (SEM). Additionally, micro-hardness and wear tests executed to understand performance of clad-substrate system.

 

Лазерното покриване (ЛП) е важна, нововъзникваща адитивна производствена технология при поправката на шанци и матрици. Тя предоставя алтернатива на традиционните техники, базиращи се на отлагане. За да се повиши живота на шанците е било наблюдавано, че поправките, проведени с технологията на лазерно покриване са по-добри от тези проведени чрез заваряването или термично пръскане. В тази работа е извършено експериментално изследване на лазерно покриване на H13. За поправката повърхностна повреда на H13 инструментална стоманена плоча е бил отложен слой стоманена пудра Stallite 21, чрез използването на диоден лазер, в комбинация с прахова инжекционна система. Микроструктурата на лазерно покритите проби е характеризирана, чрез оптичен микроскоп (ОМ) и сканиращ електронен микроскоп (СЕМ). Освен това тестове за микро-твърдост и износване, изпълнени, за да се разбере работата на облицовъчната система.

 

Download PDF full text